Corrosion mapping with high spatial resolution

For correlative corrosion-microstructure study

Typical XYZ-motor stage have scan resolution of 20~50 nm

Sits on anti-vibration table for noise reduction

Pulls glass electrodes with tip diameters <30 nm

Capable of pulling quartz, borosilicate and aluminosilicate glass

Fully programmable - including heating filament characteristics

Up to 350 oC, 25 MPa

Designed for corrosion for subcritical aqueous corrosion, CO2 corrosion, geothermal corrosion etc.

Oxygen and moisture controlled within a glove box 

To simulate atmospheric corrosion with well controlled relative humidity and temperature

Two channels

For various corrosion studies including linear polarization, potentiodynamic/potentiostatic/galvanostatic polarization, cyclic voltammetry, electrochemical impedance spectroscopy etc.

Potential range: from ± 10 V down to ± 30 mV. Potential resolution: from 1 µV (± 60 mV range) to 333 µV (± 10 V range)

Current range: ± 1 A to 10 nA (9 ranges). Current resolution 0.004 % of the range : 760 fA (standard)

For various corrosion studies including linear polarization, potentiodynamic/potentiostatic/galvanostatic polarization, cyclic voltammetry, electrochemical impedance spectroscopy etc.

Maximum Applied Potential - Up to +/-32V@+/-1.5A or +/-15V@+/-3A

EIS - 10 μHz - 1 MHz

For various corrosion studies including linear polarization, potentiodynamic/potentiostatic/galvanostatic polarization, cyclic voltammetry, electrochemical impedance spectroscopy etc.

Maximum Applied Potential - ±11 V

EIS - 10 μHz - 5 MHz

Qty: 5

Produce deionized water (18.25MΩ.cm@25°C) 

Produce RO water (desalination rate as high as 95-99%)

Water Flow Rate: 1.5-2L/min

Water Production Rate: 10L/H

Temperature Range: -20°C to +100°C

Temperature Stability: ±0.1°C

Capacity: 5.4-6.5 L

Capacity: 220 g

Resolution: 0.1 mg

Accuracy: ±0.01 (pH)

pH Range: -2 to 18

Temperature: 50 °C to 360 °C

Speed: 100 to 1500 rpm